Sell ELECTRODES FOR CAST IRON AWS E-NI-CI "Hyundai" - CV.CITRA HARAPAN JAYA

ELECTRODES FOR CAST IRON AWS E-NI-CI "Hyundai"

S-NCI AWS A5.15 / ASME SFA5.15 ENi-CI
JIS Z3252 DFC Ni
Preheat&Interpass Hardness
Temp. (HRB)
- 77.6
S-NCI can be used for repairing cast iron and joining of various kinds of cast iron products such as
cylinder covers, motor beds, casings and gears. Repairing of meehanite, alloy and malleable cast iron.
Applications
Characteristics on Usage
Notes on Usage
Typical Chemical Composition of All-Weld Metal(%)
AC or DC+
Welding Position Current
Packet 2.5kg (5.5 lbs)
Carton 2.5kg (5.5 lbs) 4 : 10kg (22 lbs)
Approval
C Si Mn P S Fe Ni
1.38 0.79 0.36 0.004 0.003 0.58 98.3
S-NCI is a graphite type coated electrode, depositing nickel weld metal. Hardening of heat affected
zone is small and machining of the welds is comparatively easy. Therefore it is suitable for welding
alloy cast iron of poor weldability, malleable cast iron and hydraulically pressured parts as well as
common cast iron.
Chip off base metal completely at the repairing part.
There is a possibility that cracks spreads or makes holes at both ends of repairing part.
Keep the weld metal length less than 50mm(2 inch) to disperse welding heat. Adopt back
stepping stone or symmetry method by turns.
Hot peen in every pass.
The preheat temperatures vary in accordance with the size, kind and shape of base metal. 150
(302 ) is appropriate in general.
Packing
Typical Mechanical Properties of All-Weld Metal
Sizes Available and Recommended Currents (Amp.)
Size mm (in)
Length mm (in)
F
2.6 (3/32) 3.2 (1/8) 4.0 (5/32)
300 (12) 350 (14) 350 (14)
58~80 80~130 110~160